The objective of this study is to investigate the influence of welding residual stresses on the fatigue crack growth behavior of cracks located transverse to the weld bead. For this purpose, G. T. A (Gas Tungsten Arc) welding was performed on hte Al alloy 1100-O plate and the same initial crack is made on HAZ(Heat Affected Zone), weld metal and base meta respectively. Specimens were used CT(Compact Tension) specimens. Initial welding residual stresses were measured by using strai gage sectioning method. All specimens were tested under constant amplitude load with stress ratio R=0.1, It is possible to predict fatigue crack growth behaviors and the fatigue life, using numerical analysis together with distribution of initial residual stress and the values of C and m obtained from da/dN-ΔK