Epidote occurs as veinlets in the propylitic alteration zone of the Bobae clay deposit, Pusan, Korea. Its cell parameters apparently decrease with the contents of Al, Fe, and Ca. Fourier transform infrared (FTIR) spectra show one hydrosyl environment related to AlM2 at 3357-3358 cm-1. In the mid-infrared region, the peaks at 950 and 1030 cm-1 sharper with increasing Al shifting to higher energy region. The peak at 885 cm-1 shifts slightly to a lower energy region with a decreasing intensity as the Fe content increases. In the far-IR region, epidote exhibits absorption bands at 120 and 140 cm-1, which are related to the Ca-O bonds in A-sites.M ssbauer spectra of epidote show that the isomer shifts of Fe3+ range from 0.36-0.37 at the M3 site and from 0.35-0.44 at M1 site. Fe2+ shows the isomer shift ranging from 1.11 to 1.13. Quadrupole splitting is 2.04 for Fe3+M3, 0.52-0.70 for Fe3+M1, and 2.61-2.70 for Fe2+M3. Calculation shows Fe3+M386-90.7%, Fe3+M12.5-3.6%, and Fe2+M35.8-11.4% of total iron, showing preferential distribution of Fe3+ in the M3 site. The Fe3+M3 content is between 0.486 and 0.513 per formula unit. in the Fe-rich epidote, less Fe3+ and more Fe2+ are accommodated in the M1 and M3 sites. Hence, the overall disorder increases as total Fe content increase. The ordering parameter of the Bobae epidote is 0.93-0.95, suggesting a disequilibrium state below 200$^{circ}C$. The constant temperature over a long period may be essential for the transition from disordered state to equilibrium state, despite the possible variation in flux and composition of the hydrothermal fluid.