Fracture strength of $Si_{3}N_{4}/20$ vol% SiC nanocomposites with fifferent sintering additives was measured. Strength of nanocomposites with 6 wt% $Y_{2}O_{3}$ and 2 wt% $Al_{2}O_{3}$ as sintering additives was higher at room temperature but significant strength degradation at elevated temperature was occured due to the softening of grain boundary phase. Fracture strength of 8 wt% $Y_{2}O_{3}$ doped sample was higher than that of $Al_{2}O_{3}$ added sample at $1400^{circ}C$. The retention of high temperature strength in 8 wt% $Y_{2}O_{3}$ doped sample can be attributed to high softening temperature and crystallization of grain boundary glassy phase.