The effects of added VC, Cr$_3$C$_2$ and TaC on the microstructures and properties of submicron WC-10%Co cemented carbides. The relative sintered density of compact was increased by addition of Cr$_3$C$_2$ but decreased oppositely by addition of VC or TaC. The growth of WC grains was significantly suppressed by addition of these carbides. The hardness of these alloys was increased by addition of other carbides and showed a maximum value by simultaneously added VC and Cr$_3$C$_2$. The transverse rupture strength(T.R.S.) was in- creased by addition of Cr$_3$C$_2$, while it was decreased by addition of VC or TaC. The relative sintered density and T.R.S. of these alloys were improved by HIP-treatment. The maximum T.R.S. was 328kg/mm$^2$ in the Wc-10%Co cemented carbide with addition of 0.5%VC.