strontium titanate (SrTiO3) thin films deposited on Pt/MgO were prepared by Plasma Enhanced Metal Orgainc Chemical vapor Deposition (Pe-MOCVD). The crystallinity of SrTiO3 thin films increased with increasing depo-sition temperature and SrF2 second phase disappeared at 55$0^{circ}C$ The films showed a dielectric constant of 177 and a dissipation factor of 0.0195 at 100 kHz. The variation of capacitance of the films with applied voltage was small showing paraelectric properties. The charge storage density and leakage current density were 40fC/${mu}{ extrm}{m}$2 and 3.49$ imes$10-7 A/cm2 at 0.25 MV/cm, respectively.