TiB2-BN-AlN composite was fabricated with the addition of 0~12 wt% WC by HP-sintering. Their sinterability. microstructure mechanical and electrical properties were studied as a function of the WC content. The addition of WC up to 12 wt% increased the flexural strength and decreased electrical resistivity as compared with those of the TiB2-BN-AlN composites. The electrical resistivity of TiB2-BN-AlN composite with 4.3 wt% WC was 640$mu$$Omega$-cm. It was found that the TiB2-BN-AlN composites with WC addition more than 4wt% was suitable for the application to the Al evaporation boat.