In order to fabricate solid electrolyte CaO-stabilized ZrO2 of high density sintered body economically 13 mol% CaO-stabilized ZrO2 powders were synthesized by the coprecipitation method. The characteristics and sintering behavior of fine powder were investigated. The precipitates has the specific surface area of 193 m2/g and apperaed to be fine and spherical primary particles with a size of approximately 5nm. The crystalliza-tion temperture of CaO-stabilized ZrO2 was 462$^{circ}C$. The tetragonal phase was stable in the low calcining tempe-rature regions and the cubic zirconia solid solution was formed from above 120$0^{circ}C$ through an intermediate stage of formation of CaZrO3 By introducing fine powders washed with alcohol and ball-milling process after calcination the sintered body was possible to attain the value of above 92% of the theoretical density at low temperature of 120$0^{circ}C$.