Shrinkage behaviors associated with forming drying and firing processes could be a driving force for the densification in materials. Low shrinkage-densification behaviors in clay materials have been shown to be highly dependent upon the processing parameters including particle size effect and kinetic behaviors caused by phases transformation characteristics. Chamottes pre-treated at 90$0^{circ}C$ and 120$0^{circ}C$ had dominent influence upon shrinkage control of materials during heat-treatment. But Coarse chamotte particles heat-treated at 120$0^{circ}C$ did not contri-bute to any densification behaviors in clay materials while these added coarse particles could enhance near-net-shape control. Microstructure / property relationships in clay materials have been thought to be directly influenced by optimized characteristics between low shrinkage and densification behaviors