In this study (Ba1-xPbx)TiO3 was synthesized by modified oxalate process in order to prevent vaporization of PbO through low temperature synthesis climinate Cl ion reproducibly substitute Pb for by and uniformly distribute ion (Ba1-xPbx)TiO3 was synthesized by coprecipitation of lead acetate barium acetate and ammonium titanyl oxalate have been used as starting materials. The substitution of Pb for Ba was reproducibly possible synthetic temperature of perovskite structure becomes lowed as the Pb concentration increases and fine partic-les (specific surface are :7.2 cm2/g) were obtained, BaTiO3 powders calcined at 90$0^{circ}C$ for 3 hours were cubic from in XRD analysis and as Pb content was increases evident split of tetragonal peaks could be observed The optimum conditions to synthesize (Ba,Pb)TiO3 powder are the followings ; synthesis temperature (5$^{circ}C$)