The spinel/cubic stabilized zirconia composites were fabricated via, The reaction sintering of monoclinic zirco-nia(baddeleyite) added with MgAl powder. During heating Mg and Al were oxidizedfirst and subsequently the oxides formed spinel (MgAl2O4) and finally remained MgO stabilized the zirconia, Because the oxides formed during the oxidation process would have very fine grain size (order of submicron) mainly due to the effects of attrition milling the reaction sintering was more effective in densification and improvement of strength and fracture toughness than conventional sintering with direct addition of MgO. The sintering behavior phase transformation during firing and mechanical properties of sintered body were investigated with emphasis on the relations between spinel formation due to MgAl addition and sintering and mechanical properties.