Polyester yarns and fabrics containing three levels of $TiO_2$ delusterant were hydrolyzed with NaOH and examined for physical and morphological changes. The mechanical propertis and hand values of alkaline hydrolyzed polyester fabrics were measured using KES-FB system. Also, the relationship between the morphology and the mechanical property of alkaline hydrolyzed polyester fabrics was analyzed. The results are as follows: 1. At an initial stage of alkaline treatment, the concentration of $TiO_2$ did not affect the weight loss of the treated yarns. But by increasing treatment time, the effect of the concentration of $TiO_2$ on the weight loss of the fiber became more pronounced. The weight loss were increased in the following order; fulldull> semidull> clear 2. The effect of hydrolysis on yarn tensile strength seems to be more related to the size of the pits on the fibers rather than the number of pits. 3. Axially oriented pits occurred along the hydroyzed, delustered fiber surfaces, while such pitting was absent on hydrolyzed fiber containing no $TiO_2$. The number of voids across the surface of a fiber increased with an increase in the amount of TiOa incorporated into the fibers. The size of the voids depended on the treatment time of hydrolysis rather than the concentration of TiOa. 4. The mechanical properties and hand values of polyester fabrics were changed by alkaline treatment but were identical regardless of the concentration of TiOa. While the mechanical properties of polyester fabrics depended on the structural change of the fibers and the yarns within the fabrics as the fiber diameter became progressively smaller rather than the size and number of pits.