M type hexa-ferrites were prepared by means of a solid state reaction using mill scale, $Fe_{2}O_{3}$, and the mixture of mill scale and $Fe_{2}O_{3}$. The mixture of powders were calcined at $1150^{circ}C$ for 2 hrs. and sintered at $1250^{circ}C$ for 2 hrs, with varing the mole ratio of $Fe_{2}O_{3}$/$BaCO_{3}$, by 5.2~6.0. And the magnetic properties and morphologies of Baferrites with impurities such as $SiO_{2},;Al_{2}O_{3},;MgO,;CaO;and;Na_{2}O$ in the mill scale were investigated. The magnetic properties were worsened by the addition of $Na_{2}O because of non-reacted iron oxide and intermediate compound of $BaFe_{2}O_{4}$ but they were improved apparently by the addition of $Si_{2}$ and $Al_{2}O_{3}$ in the composition of $BaO.5.6Fe_{2}O_{3}$. Moreover, $M_{s}$ decreased but $_{B}H_{C}$ increased through the addition of $Al_{2}O_{3}$ in Ba-ferrite. ${(BH)}_{max}$ of sintered BM($BaCO_{3}$, mill scale mixture) and BFM($BaCO_{3}$, $Fe_{2}O_{3}$, and null scale mixture) were 0.86 and 1.04 MGOe, respectively, and the magnetic properties were changed around $440^{circ}C$.