In the present paper, the Cu films 4.mu.m thick were deposited by RF magnetron sputtering method on Si wafer. The Cu films deposited at a condition of 100W, 10mtorr exhibited a low electrical resistivity of 2.3.mu..ohm..cm and densed microstructure, poor adhesion. The Cu films grown by 200W, 20mtorr showed a good adhesion property and higher electrical resistivity of 7.mu..ohm..cm because of porous columnar microstructure. Therefore, The Cu films were deposited by double layer deposition method using RF magnetron sputtering on Si wafer. The dependence of the electrical resistivity, adhesion, and reflectance in the CU films [C $U_{4-d}$(low resistivity) / C $U_{d}$(high adhesion) / Si-wafer] on the thickness of d has been investigated. The films formed with this deposition methods had the low electrical resistivity of about 2.6.mu..ohm..cm and high adhesion of about 700g/cm.m.m.