We have investigated dielectric properties of low fired ceramics BiNbO$_{4}$ containing 0.05[wt%] V$_{2}$O$_{5}$ and x[wt%l Cr$_{2}$O$_{3}$ (x=0, 0.2, 0.4, 0.8, 1.2). By substituting Cr for Bi, dielectric constant .epsilon.$_{r}$ and quality factor Q.f increased and temperature coefficient of resonant frecquency .tau.$_{f}$ changed to positive value. In the composition of BiNbO$_{4}$+0.05 [Wt%] V$_{2}$O$_{5}$+0.8[wt%]Cr$_{2}$O$_{3}$ sintered at 960[.deg. C], we could obtain microwave dielectric properties of .epsilon.$_{r}$=49, Q.f.simeq.3000[GHz](at 4.8[GHz]), .tau.$_{f}$.simeq.0[ppm/.deg. C]. As the above ceramics can be sintered near 960[.deg. C], it is applicable to multilayer microwave device with Ag conductor.tor.tor.tor.