Indium-tin oxide (ITO) films were deposited on the glass substrate by the reactive -ionized cluster beam deposition(ICBD) method. In the oxygen atmosphere, indium cluster formed through the nozzle is ionized by the electron bombardment and is accelerated to be deposited on the substrate. And tin is simultaneoulsy evaporated from the boron-nitride crucible. The chracteristics of films were examined by the X-ray photoelectron spectroscopy(XPS), glancing angle X-ray diffractrion(GXRD) and the electrical properties. were measured by 4-point-probe and Hall effect measurement system . From the XPS spectrum , it was found that indium and tin atoms combined with the oxygen to form oxide$(In_2O_3, SnO_2)$. In the case of films with high tin-concentration, the GXRD spectra show that the main $In_2O_3$ peak of (222) plane, but also sub peaks((440) peak etc.) and $SnO_2$ peaks were detected. From that results, itis concluded that the heavily dopped tin component (more than 14 at. %) disturbs to form $In_2O_3$(222) phase. Four-point-probe and Hall effect measurement show that, in the most desirable case, the transmittance of the films is more then 90% in visible range and its resistivity is $$ ho$=3.55 imes10^{-4}Omega$</TEX>cm and its mobility is $mu$=42.8 $ extrm{cm}^2$/Vsec.