The purpose of this investigation is to estimate the strength with the variations of the notch shape and the adgesive condition at the fiber/matrix micro interface of E-glass/PP laminates. To promote the degradation of the adhesive condition at the fiber/matrix micro interface without matrix dissolution loss, low-, hot-wet and spiking tests were carried out. The absorpotion properties and the tensile properties were compared accrding to the fiber orientation and the content. The results show that, firstly, saturated moisture absorption was reached at 5cycles and their absorptions of RD-40, UD-42 and UD-50 are 0.68%, 0.63%, 0.60%, respectively. Secondly, all the specimens investigated were mostly degraded at 5cycle, whereas UD-50 having ellipse shaped notch the least decrement of strength.