In this research, to develope the A1 7075/CFRP multilayered hybrid composites, CRALL(Carbon Reinforced aluminum lamiate) specimens were processed by autoclavecuring system that curing temperature, time, surface pretreatment condition of aluminum were constant. Andthe fatigye life and failure mechanism on CFRP volume fraction and fiber orientation of CRALLspecimens were investigated. A fatigue life was greatly influenced by effect of CFRP fiber volume fraction but it was less effected than those of fiber orientation. The fatigue failure arised from interface delamination of CFRP and aluminum sheet after shear fracture of aluminum layer. The failure mechanism is assumed that the aluminum laminates which divide the CFRP into many thim layers tend to arrest the failure propagation.