For the fabrication of the circuits, contact or terminal areas are usually coated with nickel and gold. Usually, diluted palladium solution is applied to initiate electroless nickel plating on the copper circuits. However, the trace amounts of palladium remains on the resin and it causes the extraneous deposition. We confirmed that selectivity was greatly improved by the treatment with the strong reducing agents such as SBH or DMAB. Bondability was greatly influenced by the contents of phosphorus in the deposited nickel. Stabilizers in the electroless gold plating were also influenced the bonding strength. The baths containing cupferron or potassium nickel cyanide as a stabilizer showed superior bondability. The gold deposits having strong orientation with Au(220) and Au(311) showed good bond ability.