Electrolytic impregnation of nickel hydroxide into porous sintered nickel plaque from various nickel solutions were carried out at room or high temperatures and current density range of 2.5mA $cm^{-2}$ to 25mA $cm^{-2}$. The morphology of the deposited surface was observed with an electron microscope and the surface products were analyzed by means of X-ray diffraction method. Nickel hydroxide was deposited in nickel nitrate electrolyte, while deposits from sulphate or chloride solutions were almost metallic nickel. The loading level of nickel hydroxide from nitrate solutions was 1.6g$cm^{-3}$ void volume and the appearance of the surface was good quality. Discharge capacity of prepared electrodes in nickel nitrate electrolyte was larger than that of the others bath. It was considered that the cell capacity was dependent on the surface roughness of active material.