Austenite stainless steel was produced by arc welding with current 650A, voltage 50V and welding speed 10cm/min. It was post-welded and then heat treated at $1,050^{circ}C$ for 120min. And then it was immersed in water or in air. The microstructural changes, ferrite contents, mechanical properties, and stress corrosion cracking(SCC) were investigated. The SCC was studied in 42wt% boiling $MgCl_2$($140^{circ}C$) under the constant stress using SCC elongation curve. The results showed that; 1. The as-welded spedimen seemed to increase ${delta}$-ferrite content largely, and revealed continuous network of lathy and vermicular type. The post-welded heat treatment changed the morphologies of ferrite from continuous type to island type. 2. The as-welded, air and water quenched specimens had the ${delta}$-ferrite content 9.7%, 3.2% and 2.1% respectively. We also showed that ${delta}$-ferrite was Cr-rich and Ni-poor by EPMA. 3. The time of failure on the SCC was measured and it was used for corrosion elongation curve. The condition of SCC was investigated under $35kgf/mm^2$ load and the results were as follows; 4. The intergranullar cracking by stress corrosion was most distinct in weld metal while the transgranular cracking occurred in the air cooled specimen.