The carbide growth behavior of MAR-M247 LC alloy was investigated by directional solidification and quench method. The carbide volume fraction, trapping and growth behavior were correlated with the growth rate. It was found that the carbide volume fraction decreases at slower growth rate. This decreasing was caused by lower solid-liquid interface trapping ability at the slower growth rate.