To make good use of chitosan forming complex with heavy metals in wood preservative treatment, woods impregnated with chitosan and copper sulfate were prepared. Amounts of leached copper, decay resistance, anti-mold efficacy, iron corrosion rates, moisture regain rates and degradation pattern in chitosan pre-treated and untreated wood were compared. After leaching test, amounts of leached copper from chitosan pre-treated wood had a much smaller than chitosan untreated wood, and good decay resistance was retained even after leaching test. From these results, it was proved that chitosan-copper complex formed in wood played and important role for decay durability. In chitosan pre-treated wood, damage values by test molds became remarkably smaller, but the growth of test molds was not perfectly inhibited. Distinct differences in iron corrosion rates between chitosan pre-treated and untreated woods was not recognized but chitosan pre-treated wood showed the lower moisture regain rates than chitosan untreated wood because of water insoluble chitosan membrane formed in wood. After leaching test, the tracheid walls in the wood treated with 2.0% copper sulfate only were eroded by the fungal attacks, but those in the wood pre-treated with chitosan remained almost intact.