Abrasive wear characteristics of high Cr white cast iron-based hardfacing were investigated using the rubber wheel abrasion wear test method according with the ASTM G65-85. Mild steel was also tested for comparison with high Cr cast iron hardfacing. Wear experiments, where the applied force, wheel revolution rate and abrasive powder feed rate were selected as test valuables, were planned and analyzed by response surface method to evaluate wear statistically and quantitatively. Weight loss of high Cr cast iron hardfacing was mostly affected by the applied force and wheel revolution rate, and little by the powder feed rate. Weight loss of mild steel was greatly affected by the wheel revolution rate and powder feed rate, and slowly and steadily increased with the applied force. Abrasive wear mechanism of high Cr cast iron and mild steel was discussed in the light of the wear test results.