An experimental study of the application of Silica fume for the high strength concrete was conducted. Nine specimens with three different contents of silica fume, 0%, 10%, 20% and with three water-cement ratio 30%, 40%, 50% were tested. Results shows that 10% of silica fume and 30% of water-cement ratio has a maximum strength with 700kg/$cm^2$ of compressive strength and 64kg/$cm^2$ of splitting tensile strength and 100kg/$cm^2$ of flexural strength. Slump value of the tested samples decreases with increasing water-cement ratio and elapsed time of silica fume. Splitting tensile strength$({sigma}_f)$ and flexural strength $({sigma}_f)$ and static modulus of elasticity(E) can be correlated with compressive strength $({sigma}_c)$ from a regression analysis.