$Cu-Al_20_3 $ composite powders were prepared by hydrogen reduction of $Cu^{2+}$ from ammoniacal copper sulfate solution on alumina core using autoclave. The copper reduction rate and the properties of copper layer were investigated using Scanning Electron Microscope(SEM), X-ray diffractometer, size and chemical analyzers. The reduction rate of $Cu^{2+}$ showed the maximum value when the molar ratio of [$NH_3$]/[$Cu^{2+}$] was 2. In order to prevent the agglomeration of Cu powder and ethane reduction rate, $Fe^{2+}$ and anthraquinone which act as catalysis were added in the solution. Catalysis was effectively chanced with the addition of two elemerts at a time. Optimum conditions obtained in this study were hydrogen reduction temperature of 205$^{cire}C$, stirring speed of 500 rpm and hydrogen partial pressure of 300 psi. Obtained $Cu-Al_20_3 $ composite Powders were found to have the uniform and continuous copper coating layer of nodule shape with 3~5 $mu$m thickness.