Cu-brazed layer between the sintered-cam(Fe-5Cr-lMo-0.5P-2.5C, wt%) and seamless steelpipe(0.25-0.35C, 0.3-1.0 Mn, bal Fe, wt%) in the camshaft shows a columnar structure of $gamma$-phase growing from the steel pipe. Liquid phase sintered 60Fe-40Cu alloys are carburized to simulate the brazing process giving rise to the columnar growth. Liquid film migrations and columnar growth of $gamma$-grains are observed in the carburized regions. The $gamma$-grains grow in the same direction as the C-diffusion. Fe-solubility in the liquid of carburized region is higher than in the uncarburized by about 0.3 at%. The columnar growth is driven by the gradient of the supersaturated Fe-solute in the liquid between two adjacent $gamma$-grains.