Because of the novel characteristics such as chemical stability, hardness, electrical resistivity and thermal conductivity, diamond-like carbon (DLC) film is a suitable material for the passivation layers. For this purpose, using the PECVD, DLC films were synthesized at room temperature. The adhesion and the hardness of the DLC films deposited on Si an SiO2 substrate were measured. The resistivity of 5.3$ imes$$10^8$$Omega$.cm was measured by automatic spreading resistance probe analysis method. The thermal conductivities of different DLC films were measured and compared with that of phospho silicate glass (PSG) film which is commonly used as passivation layers. The thermal conductivity of DLC film was improved by increasing hydrogen flow rate up to 90 sccm and was better than that of PSG film. The patterning techniques of the DLC film developed using the RIE and the lift-off method to form 5$mu extrm{m}$ line. Finally, the thermal characteristics of the power transistor with the DLC film as passiviation layer was analyzed.