Tetragonal zirconia polycrystals (TZPs) doped with $Y_{2}O_{3}$ and $Nb_{2}O_{5}$ were prepared by the conventional sintering to enhance fracture toughness and phase stability of TZPs without controlling the grain size. TZP composites were obtained by adding the transformable TZP to the non-transformable TZP in wt%. The monolithic tetragonal $ZrO_2$, same as the composite composition containing 15 wt% transformable TZP, sintered at $1550^{circ}C$ for 10h in air, exhibited the fracture toughness of 9$MPam^{1/2}$ and no low-and high-temperature degradation at temperatures in the range of 220 to $1000^{circ}C$ for 100h in air. The corresponding single composition was 90.24 mol% $ZrO_2$-5.31 mol% $Y_{2}O_{3}$-4.75 mol% $Nb_{2}O_{5}$. The microstructure observation revealed that the t-$ZrO_2$ grains grew grandually with sintering time and no microcraking and twinning were observed.