Coal tar pitch was used to study the effect of the pyrolysis conditions to produce mesophase pitch used as a matrix precursor for carbon/carbon composites. The pyrolysis conditions were presented in all cases that the total pressure was 1 atm and the first stage temperature was changed from 25$0^{circ}C$ to 34$0^{circ}C$ to remove the low molecular weight compounds in the pitch, and then, heated to 40$0^{circ}C$ to form anisotropic mesophase as the second stage temperature. The first stage temperature was very affected to form resulting anisotropic mesophase pitch. The resulting mesophase pitches show a significantly increased anisotropic contents upto 30$0^{circ}C$. However, the contents of mesophase were decreased above 30$0^{circ}C$. It was the reason that the first stage temperature had been control the number of free radicals to react the aromatic compounds in the pitch to form high molecular weight compound. Therefore, the two stage pyrolysis method could be very effectively used to control various contents of anisotropic polyaromatic mesophase compared to continuous to continuous heating method.