Effect of particle size of alumina and amount of talc on tape casting and densification behaviors of alumina-talc system were investigated. The pseudoplastic behaviors of slurries increased with increase in amount of talc addition and decrease in alumina particle size. In case of using coarse alumina powder, densification of specimens were accelerated with increase of sintering temperature and amount of talc addition. On the contrary, fine alumina powder retarded of rearrangement of alumina particle during liquid phase sintering due to premature densification of alumina matrix region before formation of liquid phase and then densification of specimens were suppressed with increase of sintering temperature and amount of talc addition.