Silicon carbides with self-reinforced microstructure which hore a small grain matrix and dispersed large grains with rod-like type were prepared by the liquid-phase sintering and the control of starting phases of raw materials. The specimens with self-reinforced microstructure could be obtained from the compacts with mixed compositions of $alpha$-SiC and 10-50 % $eta$-SiC powders and by the pressureless sintering at 185$0^{circ}C$ for 5h. Large grains with rod or plate-like types were 4H-SiC and small grains with equi-axed type were 6H-SiC. Fracture grains with rod or plate-like types were 4h-SiC and small grains with equi-axed type were 6H-SiC. Fracture toughness of specimens with self-reinforced microstructure was increased by the crack deflection and formation of microcracking due to the existence of rod-like large grains during crack propagation.