The purpose of this article is to investigate the effect of $O_{2}$ low temperature plasma treatment oft chitosan treatment of polyester fabrics. Moisture regain, static charge, crease resistance and reduction ratio of the treated fabric were measured. The results of this study were as follows: The add-on ratio and. the moisture regain of polyester fabrics treated with chitosan after treated by plasma(CP PET) were higher than those of polyester fabrics treated with only chitosan(C PET). The static charge of polyester fabrics decreased greatly with increasing the concentration of chitosan. A durability for laundering of CP PET was higher than those of C PET. The crease resistance of polyester fabrics decreased with ihcreasing the concentration of chitosan continuously. CP PET had higher decreasing rate and better durability than C PET. It showed that chitosan-treated polyester fabrics had over 90% reduction ratio after 10 times of laundering, and CP PET had better reduction ratio than C PET.