The various deformation and fracture behaviors under light loads in soda-lime glass under sliding Vickers indentation have been studied. In soda-lime glass, deformation and fracture behaviors can be classified into four different patterns by applied load. At very light load (<0.1N), plastic deformation only occurred. At low loads (0.1~0.8N), median crack, appear. At intermediate loads (0.8~3.0N), median and lateral cracking occurred leading to a large chipping. At high loads (3.0~6.0N), a crushed zone was observed with median crack. The friction experiment finds that the increasing in the friction coefficients coincides with the onset of crushing in soda-lime glass.