In order to establish a new temperature criterion to prevent the pistons from ring sticking due to deposit formation, bench test and engine test were performed. The effects of oil degradation and temperature on deposit formation was studied by a modified panel coking test. Oil degradation was analyzed by FTIR. Oil oxidation and nitration were selected as a factors to evaluate oil degradation. Bench test results show that oil oxidation is more effective to the deposit formation than oil nitration. And the temperature increase accelerates deposit formation and deposit formation increase rapidly above 26$0^{circ}C$. Especially, in case of degraded oil, the deposit formation increases so rapidly that ring sticking can occur. The effect of piston temperature on the deposit formation was confirmed by engine test.