The th ermal and optical properties of multicomponent oxide glass optical fiber by adding heavy metal oxide Ga$_{2}$O$_{3}$(0-20wt%) were investigated. The fiber samples were made by the method of rod in tube. The optical loss of fiber was measured in 0.3-1.8.mu.m wavelength region. As Ga$_{2}$O$_{3}$ increased up to 20wt%, the transition and softening temperature of bulk glass were increased from 495.deg. C to 579.deg. C and from 548.deg. C to 641.deg. C, respectively. Whereas the thermal expansion coefficient was decreased from 102 to 79.1x10$^{-7}$ /.deg. C. The refractive index was increased from 1.621 to 1.665, and IR cut-off wavelength was enlarged from 4.64.mu.m to 6.1.mu.m. The optical loss of fiber was remarkably decreased in 1.146.mu.m-1.8.mu.m wavelength region.