In order to improve the brightness and chromaticity of green emitting low voltage phosphor for FED, we examine PL, PLE and CL emission characteristics of ZnGa$_{2}$O$_{4}$:Mn,O prepared in Ar and vacuum. ZnGa$_{2}$O$_{4}$:Mn,O sintered in vacuum shows about 16 times as bright as the one fabricated in Ar and excellent chromaticity. In PL emission spectra of ZnGa$_{2}$O$_{4}$:Mn,O at low temperature of 9 K, two peaks are observed at 504 nm and 513 nm. At room temperature, the two peaks are superimposed due to the lattice thermal vibrational energy, and only one peak is observed at 509 nm. From PLE measurements, it is believed that the energy levels of the host lattice and Mn ions are coexisted. The energy transfer from the host lattice to the emission center of Mn$^{2+}$ ions occurs.s.