The transparent conductiong thin films of tin oxides were prepared on pyrex glass substrates by the pulse laser deposition. In the atmospheres of vacuum, O2, and $Sn(CH_3)_4$ a polycrystalline $SnO_2$ target was ablated by Nd-YAG laser beam to deposit thin films on the substrates at room temperature, and as-deposited films were subsequently heat-treated in the air for 2 h at 230, 420 and $610^{circ}C$, respectively. The characteristics of the thin films were examined by UV-VIS-NIR spectrometry and X-ray diffractometry, and the electrical properties were measured by four-point probe method along with film thickness monitored by the stylus method. It was observed that in the presence of $Sn(CH_3)_4$, $SnO_2$ phases were grown even at room temperature. This suggests that the microplasma producted during the laser ablation plays an important role in the dissociaation of precursor molecules.