The composition, the preferred orientation and the magnetic properties of the CoFeCu alloys electrodepositen under various electrolysis conditions in sulfate baths ware investigated. As the D.C. current density increased, the Co content in alloy electrodeposits increased, while the Cu content decreased and Fe content remained content. The effect of magnetic field up to 300 Oe on the composition of alloys was negligible. The Cu content of the alloys deposited in pulse current increased noticeably with increasing off-time, while the Co and Fe content decreased. The coercivity of the alloys with 3.5 to 7.0wt.% Cu was 1.0 to 2.0 Oe, but increased noticeably above and below that composition. The application of magnetic field during deposition decreased the coercivity of alloys. The saturation flux density of the alloys with 3.5 to 5.0wt.% Cu was relatively high in the range from 16 to 20.7Gauss. The anisotropy field(HK) of the alloys deposited under the magnetic field(50∼300 Oe) ranged from 18 to 22 Oe. The alloys had fcc structure with (111) preferred orientation, whose distribution increased a little with increasing magnetic field.