This research is to evaluate the effect of sunshine treatment on the strength in the Al 6061/AFRP hybrid composite(APAL). APAL specimens were processed by autoclave curing system under the constant condition of curing temperature, time and aluminum surface pertreatment. Aramid patched aluminum alloy can be widely used for the repair of the damage part of the aircraft. The tensile strength of the sunshine treated APAL 2P and 6P composite is 14%, 22% smaller than that of the non-treated material. The interlaminar shear strength of the APAL specimens for the adhesive length of 5mm is 24% higher than that of the APAL for the adhesive length of 10mm. In the case of APAL DS 1P material, interlaminar shear strength of the specimen which was sunshine treated for 200 hours is 21% smaller than that of the non-treated material while interlaminar shear strength of the specimen which was immersed in a 70.deg. C fresh water for 1200 hours decreases by 75.7%.