In order to evaluate the effects of aging on the ignition performance, pyrotechnic igniters were separated from twelve-year-old, fifteen-year-old, and sixteen-year-old live rocket motors. The characteristic values of the ignition material were measured, and the firing tests of the igniters were performed. The moisture content, the outer dimension, the crush strength, the thermal decomposition characteristics, and the heat of formation the B/$KNO_3$ ignition pellet were measured. The crush strength was increased and the heat of formation was reduced as aged, but no change was detected for other characteristic values. The burning test results of the igniter pellet in the closed bomb and the inert motor showed that the burning rate of the ignition pellet was increased by 10%, and the integration of pressure $P_t$ of the p-t curve was reduced by 15% for aged samples. It was inferred that the burning rate was increased as the crack was appeared in the pellet and $P_t$ could be proportionally decreased with the heat of explosion.