Y-zeolite and ${gamma}$-Al$_2$O$_3$ were used as supports on CO and $C_3$H$_{6}$ oxidation for diesel emission control. The catalysts composed of Pd and Pt as active components were wash coated on honeycomb type ceramic substrate. The oxidation of CO and $C_3$H$_{6}$ was carried out over prepared honeycomb in a fixed bed continuous reactor in the temperature range of 20$0^{circ}C$~50$0^{circ}C$ and 20,000 GHSV (h$^{-1}$ ). Surface area of Y-zeolite was larger than that of ${gamma}$-Al$_2$O$_3$ due to channel structure of Y-zeolite. Therefore, high conversion of CO and $C_3$H$_{6}$ could be obtained because of good dispersion of active metals over Y-zeolite. The honeycomb used Y-zeolite as a support showed higher $C_3$H$_{6}$ conversion than that of ${gamma}$-Al$_2$O$_3$ due to better cracking and isomerization activity of Y-zeolite. PdPt catalyst showed high conversion of CO and $C_3$H$_{6}$ at low temperature region, 20$0^{circ}C$~30$0^{circ}C$, for their synergy effects. PdPt/Y-Zeolite catalyst could achieve more than 80％ conversion of $C_3$H$_{6}$ at 30$0^{circ}C$. The use of Y-zeolite as a support increased CO and $C_3$H$_{6}$ conversion, and decreased SO$_2$ conversion very effectively. Y-zeolite found to have a good adaptability as a support for the diesel emission after treatment system.