[ ${gamm}-Glycidoxy$ ] propyl trimethoxy silane, CTBN rubber(carboxyl terminated butadiene acrylonitrile rubber) and GMA(glycidyl methacrylate) were reacted on the surface of silica one by one in existence of TEA(triethylamine) or BPO(benzoyl peroxide). The amount of reactant was $2.5{sim}5.8%$ of treated silica weight. The treated silica was mixed with epoxy resin and MTHPA(methyl tetrahydro phthalic anhydride) in the range of $0{sim}60%$(wt.%) of total component. The thermal properties were tested for cured products. By using silica treated with silane/rubber or silane/rubber/vinyl, comparing with 3% of rubber mixed directly, it had 13% higher $T_g$ and 10% lower thermal expansion coefficient at $35{sim}55%$ of silica contents.