Since the rigid and continuous networks of high-purity silica(white carbon) were relatively transparent to microwaves, high purity silica coupled with microwaves using a zirconia susceptor at room temperature and it was then heated to its melting temperature. The low-purity silica, contained small amount of impurities, yielded greater microwave absorption owing to easy motion of the interstitial alkali ions and it was then heated to its melting temperature. X-ray diffraction patterns of the low-purity silica were broader than those of the high-purity silica due to higher concentration of non-bridging bond and more deformed random network structure. In the vulcanization process of whitened or coloured rubber compound which is employing low-purity silica(white carbon) as a reinforcing filler, vulcanizate could be obtained effectively by microwave heating energy.