Flake graphite cast irons with the high damping capacity have been used for the control of vibration and noise occuring in the members of various mechanical structures under vibrating conditions. However, the damping capacity which is morphological characteristics of graphite is one of the important factors in reducing the vibration and noise, but hardly any work has deal with this problem. Therefore, the authors have examined the damping capacity of various cast irons with alloying elements and studied the influences of the matrix, mechanical properties and morphological characteristics of graphite. The main results obtained are as follows: Effects of Ni on the damping capacities and mechanical properties are investigated in 3.9%C-0.3% Cu gray cast iron. At 0.2% Ni content, specific damping capacity showed the maximum value, and decreased with further increase in Ni content, Graphite continuity also showed same behavior. This indicates that the specific damping capacity has a close relation with graphite continuity. On the other hand, the damping capacity in pearlite matrix showed superior to that in ferrite. In contrast, with increasing the Ni content, both tensile strength and hardness increased due to the decrease of graphite length and eutectic cell size.