The bond strengths of composite resin to tooth dentin vary with the methods of cavity preparation and surface treatment. Recent developments in techniques of dentinal surface treatment have renewed interest in microabrasive as a means of tooth preparation, The purpose of this study was to determine the effects of a new method of cavity preparation on the bond of composite resin to dentin. Freshly extracted 144 healthy human third molars were used in this study. The dentin surfaces prepared with #600 SiC abrasive paper were divided into control and air abrasion groups according to the method of dentin surface preparation using different combinations of delivery pressure, time, and acid etching. The shear bond strengths were measured after the composite resin (Clearfil Photo Bright) was bonded to prepared dentin surfaces by light-curing using a dentin bonding system (All-bond 2), In addition, the average surface roughness was measured to investigate the effect of differently prepared dentin surfaces on the shear bond strengths. The surface changes of prepared dentin and the debonded dentin surfaces were observed with SEM (S-2300, Hitachi Co., Japan). The following results from this-study were obtained ; 1. There was no significant difference of shear bond strengths according to the changes of delivery pressure and time. 2. The shear bond strengths were lower than the control in the air abraded-only groups, but those of the additional acid-etched groups were higher than the control. 3. The shear bond strengths to all air-abraded surfaces were increased by acid etching. 4. The correlation between shear bond strengths and surface roughness was not certain, although the mean surface roughness of all air-abraded surfaces has increased evidently while it has slightly decreased for additional acid etching. 5. On SEM examination, the dentinal tubules were almost occluded in the air abraded-only groups, but those were opened in the additional acid-etched groups. 6. The debonded surfaces were showed adhesive failure mode in the air abraded- only groups, while those were showed mainly the mixed and cohesive failure mode in the additional acid-etched groups. These results suggest that the layer produced during cavity preparation or surface treatment with air abrasion must be removed for maximum bond strength of composite resin to dentin.