The changes of microstructures, morphology of sclerotic dentin and bonding aspects generated by an adhesive resin was investigated. Incisors and premolars showing natural cervical abrasions were collected and conditioned with 10 % phosphoric acid or 10 % maleic acid. The sclerotic dentin specimens were then rinsed and blot-dried and applied with dentin adhesive (All Bond 2) to the conditioned dentin surface. To examine the morphologic change of the sclerotic dentin specimen after etching and bonding procedure, the treated specimens were examined by SEM. To analyze the chemical composition of sclerotic dentin and crystals occluding dentinal tubules, the sclerotic dentin specimen was powdered and examined with X-ray Diffractometer. To investigate the Ca/P weight percent ratio within the dentinal tubules, the sclerotic dentin specimen was fractured perpendicularly to the long axis of the tooth from the center of cervical abrasion lesion and then examined with EDX(Energy Dispersive X-ray) microanalyzer. The results were as follows : 1. The increased width of peritubular dentin and the depositions of the irregular amorphous materials within the dentinal tubules were showed in the sclerotic dentin specimens. 2. After the treatment of sclerotic dentin specimen with 10 % phosphoric acid or 10 % maleic acid, the lateral side of tubules rather than cross-sectional tubule openings was showed exclusively at the incisal and gingival incline of the specimens. 3. After the treatment of sclerotic dentin specimen with 10 % phosphoric acid or 10 % maleic acid, the hybrid layer was not formed evidently and the resin tag was not formed or shortly penetrated into the tubules with the thinner diameter. 4. According to the results of XRD analysis of the sclerotic dentin specimen, Hydroxyapatite and Octacalcium phosphate were predominent, however, Whitlockite crystals were rare. 5. The mean Ca/P weight percent ratio analysed from 5 fractured sclerotic dentin specimens was $2.322{pm}0.170$ at the intertubular dentin, $1.826{pm}0.051$ within the dentinal tubule.