Resin modified glass ionomers were introduced in 1988 to overcome the problems of moisture sensitivity and low early mechanical strength of conventional glass ionomers and to maintain their clinical advantages. The purpose of this study was to evaluate the color stability of four resin modified glass ionomers(Fuji II LC, Vitremer, Dyract and VariGlass), one resin composite material(Z-100), and one conventional glass ionomer(GC Fuji II) under several conditions. These conditions were as follows: 1) before curing, 2) after curing, 3) after polishing, 4) after 500 thermocycling, 5) after 1,000 thermocycling, 6) after 1,500 thermocycling and 7) after 2,000 thermocycling. Three specimens of each material/shade combination were made. Materials were condensed into metal mold with a diameter of 10 mm and a thickness of 2.0 mm, and were pressed between glass plates. The material was polymerized using a light polymerizing unit(Visilux II, 3M, USA). After removal of excess, the surface was polished sequentially on wet sandpapers. A reflection spectrophotometer(Model TC-6FX, Tokyo Denshoku Co., Japan) was used to determine CIELAB coordinates($L^*,a^*$ and $b^*$) of each specimen. CIE standard illumination C was used as the light source. The results were as follows : 1. In comparing different shades of same material, CIELAB color difference(${Delta}E^*$) value was not significantly different from each other(p>0.05). 2. CIELAB color difference(${Delta}E^*$) values between after-curing and after-polishing were ranged from 5.53 to 27.08. These values were higher than those of other condition combinations. 3. CIELAB color difference(${Delta}E^*$) values between before-thermocycling and after-thermocycling were ranged from 1.40 to 7.81. Despite the number of thermocycling increased, CIELAB color difference(${Delta}E^*$) value was low. 4. The color stability of resin modified glass ionomers was more stable than that of conventional glass ionomers but less stable than that of Z100.