The purpose of this study is to observe the corrosion characteristics of five dental amalgams(CAULK FINE CUT, OPTALLOY II, DISPERSALLOY, TYTIN, and VALIANT) in the solutions with fluoride compound through the anodic polarization curve obtained by using a potentiostat. After each amalgam alloy and Hg being triturated, the triturated mass was inserted into the cylindrical metal mold, and condensed by hydraulic pressure(160 kg/$cm^2$). Each specimen was removed from the metal mold. Specimens were polished with the silicone carbide grinding paper 24 hours after condensation and stored at room temperature for 1 week. The anodic polarization curves were employed to compare the corrosion behaviours of the amalgams in 0.9 % saline solution and in the saline solutions with 2.2 ppm, 0.05 %, 2 % NaF, and 8 % $SnF_2$ at $37^{circ}C$ with 3-electrode potentiostat. After the immersion of specimen in electrolyte for 30 minutes, the potential scan was begun. The potential scan range was -1500m V to + 800m V(vs. S.C.E.) in the working electrode and the scan rate was 50 mV/sec. The results were as follows, 1. The corrosion potential, the potential of anodic current peak, and transpassive potential in the saline solutions with NaF shifted to lower direction than those in normal saline solution, and the current density in the saline solutions with NaF was higher than that in normal saline solution. The differences were increased as the concentrations of NaF became higher. 2. The corrosion potential and transpassive potential in the saline solution with $SnF_2$ shifted to higher direction than those in normal saline solution, and the current density in the saline solution with $SnF_2$ was higher than that in normal saline solution after the corrosion potential. The anodic polarization curves in the saline solution with $SnF_2$ had no outstanding anodic current peak. 3. The corrosion potentials for high-copper amalgams were much higher than those for CAULK FINE CUT and OPTALLOY II in normal saline solution, but, as the concentrations of fluoride compound became higher, the differences in corrosion potentials between them were decreased. The corrosion potentials had the similarity in the saline solution with 2% NaF or 8% $SnF_2$. 4. The current density for TYTIN was the lowest among the others in normal saline solution and in the saline solution with 2.2 ppm or 0.05 % NaF. 5. There was no significant difference in current density between Pd-enriched VALIANT and other high-copper amalgams.