This paper describes electrochemical etch-stop characteristics in THAH/IPA/pyrazine solution. I-V curves of n- and p-type Si in THAH/IPA/pyrazine solution were obtained. OCP(Open Circuit Potential) and PP (Passivation Potential) of p-type Si were -1.2 V and 0.1 V, and of n-type Si were -1.3 V and -0.2 V, respectively. Both n- and p-type Si, etching rates were abruptly decreased at potentials anodic to the PP. The etch-stop characteristics in THAH/IPA/pyrazine solution were observed. Since accurate etching stop occurs at pn junction, Si diaphragms having thickness of epi-layer were fabricated. Etching rate is highest at optimum etching condition, TMAH 25wt.%/IPA 17vol.%/pyrazine 0.1g/100ml. thus the elapsed time of etch-stop was reduced.