Adhesion of composite resin to tooth structure has been of tremendous signgicance in clinical dentistry. Due to the lack of adhesion between composite restorative resins and enamel and dentin, microleakage occurs at the tooth/restoration interface. This may lead to discoloration, secondary caries, marginal breakdown, postoperative sensitivity, and even pulpal pathology. According to extensive use of composite resin, every effort on improving bonding strength and reducing microleakage between a tooth and composite resin has been continued. This study was conducted to determine the difference in microleakage in enamel and dentin treated with air-abrasion, acid etching and combination when restored with composite resin. Class V cavities were prepared on 30 premolars. The specimens were divided into following groups. group 1:air-abrasion+Scotchbond Multi-purpose group 4 :air-abrasion+All-Bond 2 group 2:acid etching+Scotchbond Multi-purpose group 5 :acid etching+All-Bond 2 group 3:combination+Scotchbond Multi-purpose group 6 :combination+All-Bond 2 #combination:air-abrasion + acid etching The specimens were filled with Z-100 after application of Scotchbond Multi-purpose and All-Bond 2. Thermocycling was conducted by alternately dipping the specimens in $5^{circ}C$ and $55^{circ}C$ water for 30 seconds 500 times. 1% methylene blue was applied and the specimens were left for 24 hours at $37^{circ}C$. After washing out the dye, the tooth was sectioned buccolingually along the axis. The sectioned surface was observed with stereoscope for dye penetration. The author has measured the microleakage in teeth prepared with air-abrasion, acid ethching and combination to study the difference in microleakage following different methods of tooth surface treatment and has come to following results. 1. In comparing microleakage between groups, group 1 and 4 showed statistically significant difference from group 2, 3, 5 and 6(p<0.05). There was no significant difference among group 2, 3, 5, 6(p>0.05) nor between group 1 and 4(p>0.05). 2. In comparing microleakage among tooth surface treatment methods, Air-abrasion group showed significantly more microleakage than acid etching group and combination(airabrasion + acid etching) group(p<0.05). Combination(acid etching+air-abrasion)group tended to show lesser microleakage than acid etching group, but this was not statistically significant(p>0.05). 3. In comparing microleakage between bonding agents, there was no statistically significant difference between Scotch bond Multi-purpose and All-Bond 2(p>0.05).